Rare Earth Alloy Series-Magnesium Yttrium/Neodymium/Gadolinium Alloy(Mg-Y/Nd/Gd)

Specification: 300×100×65(mm), and customization

Shape: silver-white ingot, also available for customization

Packaging Method: inner lined with plastic bags, protected by argon gas, packed in iron drums, 50kg per drum

 

Specification:

Product Name	Grade	RE/%	RE impurities	Non-rare earth impurities (mass fraction/%)						Standard
				Si	Fe	Al	Cu	Ni	C
Magnesium Yttrium Alloy	Mg-Y30	30±2	0.1	0.03	0.10	0.02	0.005	0.005	0.04	GB/T 29657-2013
	Mg-Y25	25±2	0.1	0.03	0.10	0.02	0.005	0.005	0.04
	Mg-Y20	20±2	0.1	0.03	0.10	0.02	0.005	0.005	0.04
Magnesium Neodymium Alloy	Mg-Nd35	35±2	0.5	0.05	0.15	0.05	0.01	0.01	0.08	GB/T 28400-2012 HB 7264-1996
	Mg-Nd30	30±2	0.5	0.05	0.15	0.05	0.01	0.01	0.08
	Mg-Nd25	25±2	0.5	0.05	0.15	0.05	0.01	0.01	0.08
Magnesium Gadolinium Alloy	Mg-Gd30	30±2	0.1	0.02	0.10	0.02	0.03	0.01	0.03	GB/T 26414-2010
	Mg-Gd25	25±2	0.1	0.02	0.10	0.02	0.03	0.01	0.03
	Mg-Gd20	20±2	0.1	0.02	0.10	0.02	0.03	0.01	0.03

 

Product application:

1. Yttrium (Y) and Gadolinium (Gd) can significantly enhance the room temperature and high-temperature mechanical properties of the alloy through fine grain strengthening and solid solution strengthening. Besides, Yttrium (Y) can further purify the melt, reduce the oxygen (O) content, and improve the alloy's resistance to salt fog corrosion.

2. Neodymium (Nd) not only can significantly enhance the room temperature and high-temperature mechanical properties of the alloy through fine grain strengthening, but also can increase the ignition temperature, improve the alloy's casting performance and processing performance.